Ceyhun Oskay

Investigation of the microstructural and mechanical property changes of NiAl coated Ni-based superalloys during high temperature exposure

FrontBack
 
ISBN:978-3-8440-7231-0
Series:Schriftenreihe des DECHEMA-Forschungsinstituts
Herausgeber: DECHEMA-Forschungsinstitut
Frankfurt am Main
Volume:19
Keywords:Ni-based superalloys; NiAl coatings; mechanical properties; oxidation; interdiffusion
Type of publication:Thesis
Language:English
Pages:176 pages
Figures:88 figures
Weight:261 g
Format:21 x 14,8 cm
Bindung:Paperback
Price:48,80 € / 61,10 SFr
Published:March 2020
Buy:
  » plus shipping costs
Download:

Available PDF-Files for this title:

You need the Adobe Reader, to open the files. Here you get help and information, for the download.

These files are not printable.

 
 DocumentDocument 
 TypePDF 
 Costs12,20 EUR 
 ActionPurchase in obligation and display of file - 32,9 MB (34482592 Byte) 
 ActionPurchase in obligation and download of file - 32,9 MB (34482592 Byte) 
     
 
 DocumentTable of contents 
 TypePDF 
 Costsfree 
 ActionDiplay of file - 218 kB (223605 Byte) 
 ActionDownload of file - 218 kB (223605 Byte) 
     

User settings for registered users

You can change your address here or download your paid documents again.

User:  Not logged in.
Actions:  Login / Register
 Forgotten your password?
Recommendation:You want to recommend this title?
Review copyHere you can order a review copy.
LinkYou want to link this page? Click here.
AbstractThe present work focused on the determination of the mechanical behavior of aluminized Ni-based superalloys with respect to their microstructural degradation during high temperature exposure. For this purpose, a mechanical model concept was developed, which utilized Al-concentration as the major influential parameter. Mechanical properties were determined using experimental methods and were correlated with the Al-content. These experimental results were then conveyed into a software tool, which was used to determine the load-bearing capability of the coated components below and above the ductile to brittle transition temperature (DBTT) of the coating as a function of exposure duration, temperature, component and coating thickness as well as the Al-concentration in the as-deposited coating.